COMPOSITION CHIMIQUE (%) MAX | ESSAI DE TENSION | DURETÉ (HRB) MAX | ||||||||||||
LIMITE CONVENTIONNELLE D'ÉLASTICITÉ (MPA) | RÉSISTANCE À LA TRACTION (MPA) | ALLONGEMENT DANS 4D (%) | STRICTION (%) | |||||||||||
C | SI | Manganèse | P | S | Cr | Ni | MOIS | N | Autre | |||||
0.1 | 1 | 1 | 0.04 | 0.03 | 4~6 | / | 0.4~0.65 | / | / | 550 | 690 | 16 | 50 | / |
0.37~0.49 | 0.15~0.35 | 0.65~1.1 | 0.035 | 0.04 | 0.75~1.2 | / | 0.15~0.25 | / | / | 720 | 860 | 16 | 50 | / |
0.37~0.49 | 0.15~0.35 | 0.65~1.1 | 0.035 | 0.04 | 0.75~1.2 | / | 0.15~0.25 | / | / | 550 | 690 | 18 | 50 | / |
0.36~0.47 | 0.15~0.35 | 0.45~0.7 | 0.035 | 0.04 | 0.8~1.15 | / | 0.5~0.65 | / | V : 0.25~0.35 | 725 | 860 | 18 | 50 | / |
0.08 | 1 | 2 | 0.045 | 0.03 | 18~20 | 8~10.5 | / | / | / | 205 | 515 | 30 | 50 | 96 |
0.08 | 1 | 2 | 0.045 | 0.03 | 18~20 | 8~10.5 | / | / | / | 205 | 515 | 30 | 50 | 90 |
0.08 | 1 | 2 | 0.045 | 0.03 | 17~19 | / | 9~13 | / | Nb+Ta : 1OXC | 205 | 515 | 30 | 50 | 96 |
0.08 | 1 | 2 | 0.045 | 0.03 | 17~19 | / | 9~13 | / | Nb+Ta : 1OXC | 205 | 515 | 30 | 50 | 90 |
0.08 | 1 | 2 | 0.045 | 0.03 | 16~18 | 2~3 | 10~14 | / | / | 205 | 515 | 30 | 50 | 96 |
0.08 | 1 | 2 | 0.045 | 0.03 | 16~18 | 2~3 | 10~14 | / | / | 205 | 515 | 30 | 50 | 90 |
0.08 | 1 | 2 | 0.045 | 0.03 | 16~18 | 2~3 | 10~14 | / | / | / | / | / | / | / |
0.08 | 1 | 2 | 0.045 | 0.03 | 16~18 | 2~3 | 10~14 | / | / | / | / | / | / | / |
0.08 | 1 | 2 | 0.045 | 0.03 | 18~20 | 8~10.5 | / | 0.1~0.16 | / | 240 | 550 | 30 | 40 | 96 |
0.08 | 1 | 2 | 0.045 | 0.03 | 18~20 | 8~10.5 | / | 0.1~0.16 | / | 205 | 515 | 30 | 50 | 90 |
0.08 | 1 | 2 | 0.045 | 0.03 | 10~14 | 10~14 | 2~3 | 0.1~0.16 | / | 240 | 550 | 30 | 40 | 96 |
0.08 | 1 | 2 | 0.045 | 0.03 | 10~14 | 10~14 | 2~3 | 0.1~0.16 | / | 205 | 515 | 30 | 50 | 90 |